ASTM A955/A955M-16a
- standard by ASTM International, 09/15/2016
- Standard Specification for Deformed and Plain Stainless-Steel Bars for Concrete Reinforcement
- Category: ASTM
$65.00
$33.00
Full Description
1.1 This specification covers deformed and plain stainless-steel bars for concrete reinforcement in cut lengths and coils used in applications requiring resistance to corrosion or controlled magnetic permeability. The standard sizes and dimensions of deformed bars and their numerical designation shall be those listed in Table 1. The text of this specification references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the specification.
1.1.1 Supplementary requirement (S1) of an optional nature is provided. It shall apply only when specified by the purchaser. In order to obtain a controlled magnetic permeability product, steel conforming to Supplementary Requirement S1 should be ordered.
1.2 The chemical composition of the stainless steel alloy shall be selected for suitability to the application involved by agreement between the manufacturer and the purchaser. This is an important consideration in achieving the desired corrosion resistance or controlled magnetic permeability, or both, because these properties are not provided by all stainless steels.
Note 1: The alloys shown in Table 2 have found the most use in North America. Other alloys may also provide desired properties; consult with the manufacturer for stainless steel alloy properties and availability.
1.3 Requirements for the relative deformation area of three-sided deformed bars are contained in Annex A4.
1.4 Bars are of two minimum yield strength levels, namely, 60 000 [420 MPa] and 75 000 psi [520 MPa], designated as Grade 60 [420] and Grade 75 [520], respectively.
1.5 Plain bars in sizes up to and including 2 in. [50.8 mm] in diameter in coils or cut lengths, when ordered, shall be furnished under this specification in Grade 60 [420] and Grade 75 [520], respectively. Bending properties, when required, shall be by agreement between the manufacturer and purchaser. Requirements providing for deformations and marking shall not be applicable to plain bars.
1.6 Weldability of most stainless steel compositions is generally good, however, pre-weld or post-weld procedures, or both, are necessary. Where material is to be welded, a welding procedure suitable for the chemical composition and intended use or service shall be used. Retesting of physical properties should be considered following welding procedures depending upon the steel composition and welding operation involved.
Note 2: It is recommended that the user consult the manufacturer for information available from the Document HistoryProduct Details
ASTM A955/A955M-20c
ASTM A955/A955M-20b
ASTM A955/A955M-20a
ASTM A955/A955M-20
ASTM A955/A955M-18b
ASTM A955/A955M-18a
ASTM A955/A955M-18
ASTM A955/A955M-17a
ASTM A955/A955M-17
ASTM A955/A955M-16a
ASTM A955/A955M-16
ASTM A955/A955M-12e1
ASTM A955/A955M-11e1
ASTM A955/A955M-11
ASTM A955/A955M-10
ASTM A955/A955M-09b
ASTM A955/A955M-09a
ASTM A955/A955M-09
ASTM A955/A955M-06a
ASTM A955/A955M-05
ASTM A955/A955M-04ae1
ASTM A955/A955M-03
ASTM A955/A955M-04
ASTM A955/A955M-03b
ASTM A955/A955M-02
ASTM A955/A955M-01
ASTM D4377-00e1
Standard Test Method for Water in Crude Oils by Potentiometric Karl Fischer Titration..
$30.00 $60.00
ASTM E207-00
Standard Test Method for Thermal EMF Test of Single Thermoelement Materials By Comparison with a Ref..
$29.00 $58.00
ASTM D3605-00
Standard Test Method for Trace Metals in Gas Turbine Fuels by Atomic Absorption and Flame Emission S..
$25.00 $50.00
ASTM D16-00
Standard Terminology for Paint, Related Coatings, Materials, and Applications..
$29.00 $58.00