ASTM B338-08a

1.1 This specification covers the requirements for 28 grades of titanium and titanium alloy tubing intended for surface condensers, evaporators, and heat exchangers, as follows:

1.1.1 Grade 1 - Unalloyed titanium,

1.1.2 Grade 2 - Unalloyed titanium,

1.1.2.1 Grade 2H - Unalloyed titanium (Grade 2 with 58 ksi minimum UTS),

1.1.3 Grade 3 - Unalloyed titanium,

1.1.4 Grade 7 - Unalloyed titanium plus 0.12 to 0.25 % palladium,

1.1.4.1 Grade 7H - Unalloyed titanium plus 0.12 to 0.25 % palladium (Grade 7 with 58 ksi minimum UTS),

1.1.5 Grade 9 - Titanium alloy (3 % aluminum, 2.5 % vanadium),

1.1.6 Grade 11 - Unalloyed titanium plus 0.12 to 0.25 % palladium,

1.1.7 Grade 12 - Titanium alloy (0.3 % molybdenum, 0.8 % nickel),

1.1.8 Grade 13 - Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.9 Grade 14 - Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.10 Grade 15 - Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.11 Grade 16 - Unalloyed titanium plus 0.04 to 0.08 % palladium,

1.1.11.1 Grade 16H - Unalloyed titanium plus 0.04 to 0.08 % palladium (Grade 16 with 58 ksi minimum UTS),

1.1.12 Grade 17 - Unalloyed titanium plus 0.04 to 0.08 % palladium,

1.1.13 Grade 18 - Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.04 to 0.08 % palladium,

1.1.14 Grade 26 - Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.14.1 Grade 26H - Unalloyed titanium plus 0.08 to 0.14 % ruthenium (Grade 26 with 58 ksi minimum UTS),

1.1.15 Grade 27 - Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.16 Grade 28 - Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 to 0.14 % ruthenium,

1.1.17 Grade 30 - Titanium alloy (0.3 % cobalt, 0.05 % palladium),

1.1.18 Grade 31 - Titanium alloy (0.3 % cobalt, 0.05 % palladium),

1.1.19 Grade 33 - Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),

1.1.20 Grade 34 - Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),

1.1.21 Grade 35 - Titanium alloy (4.5 % aluminum, 2 % molybdenum, 1.6 % vanadium, 0.5 % iron, 0.3 % silicon),

1.1.22 Grade 36 - Titanium alloy (45 % niobium),

1.1.23 Grade 37 - Titanium alloy (1.5 % aluminum), and

1.1.24 Grade 38 - Titanium alloy (4 % aluminum, 2.5 % vanadium, 1.5 % iron).

Note 1 - H grade material is identical to the corresponding numeric grade (that is, Grade 2H = Grade 2) except for the higher guaranteed minimum UTS, and may always be certified as meeting the requirements of its corresponding numeric grade. Grades 2H, 7H, 16H, and 26H are intended primarily for pressure vessel use.

The H grades were added in response to a user association request based on its study of over 5200 commercial Grade 2, 7, 16, and 26 test reports, w

Product Details

Published:

08/01/2008

Number of Pages:

8

File Size:

1 file , 100 KB

Redline File Size:

2 files , 190 KB

Note:

This product is unavailable in Russia, Ukraine, Belarus

Document History

ASTM B338-17e1

ASTM B338-17

ASTM B338-14

ASTM B338-13a

ASTM B338-13

ASTM B338-10

ASTM B338-08a

ASTM B338-08

ASTM B338-06a

ASTM B338-06

ASTM B338-05b

ASTM B338-05

ASTM B338-03

ASTM B338-02

ASTM B338-01

ASTM B338-99