ASTM C1773-13
- standard by ASTM International, 02/15/2013
- Standard Test Method for Monotonic Axial Tensile Behavior of Continuous Fiber-Reinforced Advanced Ceramic Tubular Test Specimens at Ambient Temperatu
- Category: ASTM
$83.00
$42.00
Full Description
1.1 This test method determines the axial tensile strength and stress-strain response of continuous fiber-reinforced advanced ceramic composite tubes at ambient temperature under monotonic loading. This test method is specific to tube geometries, because fiber architecture and specimen geometry factors are often distinctly different in composite tubes, as compared to flat plates.
1.2 In the test method a composite tube/cylinder with a defined gage section and a known wall thickness is fitted/bonded into a loading fixture. The test specimen/fixture assembly is mounted in the testing machine and monotonically loaded in uniaxial tension at ambient temperature while recording the tensile force and the strain in the gage section. The axial tensile strength and the fracture strength are determined from the maximum applied force and the fracture force. The strains, the proportional limit stress, and the tensile modulus of elasticity are determined from the stress-strain data.
1.3 This test method applies primarily to advanced ceramic matrix composite tubes with continuous fiber reinforcement: uni-directional (1-D, filament wound and tape lay-up), bi-directional (2-D, fabric/tape lay-up and weave), and tri-directional (3-D, braid and weave). These types of ceramic matrix composites are composed of a wide range of ceramic fibers (oxide, graphite, carbide, nitride, and other compositions) in a wide range of crystalline and amorphous ceramic matrix compositions (oxide, carbide, nitride, carbon, graphite, and other compositions).
1.4 This test method does not directly address discontinuous fiber-reinforced, whisker-reinforced or particulate-reinforced ceramics, although the test methods detailed here may be equally applicable to these composites.
1.5 The test method describes a range of test specimen tube geometries based on past tensile testing of ceramic composite tubes. These geometries are applicable to tubes with outer diameters of 10 to 150 mm and wall thicknesses of 1 to 25 mm, where the ratio of the outer diameter-to-wall thickness (dO /t) is typically between 5 and 30.
1.5.1 This test method is specific to ambient temperature testing. Elevated temperature testing requires high temperature furnaces and heating devices with temperature control and measurement systems and temperature-capable grips and loading fixtures, which are not addressed in this test standard.
1.6 The test method addresses test equipment, gripping methods, testing modes, allowable bending stresses, interferences, tubular test specimen geometries, test specimen preparation, test procedures, data collection, calculation, reporting requirements, and precision/bias in the following sections.
| Section |
Scope | |
Referenced Documents | |
Terminology | |
Summary of Test Method | |
Significance and Use | |
Interferences | |
Apparatus | |
Hazards | |
Test Specimens | |
Test Procedure | |
Calculation of Results | |
Report | |
Precision and Bias | |
Keywords | |
Annexes |
|
Interferences | |
Test Specimen Geometry | |
Grip Fixtures and Load Train Couplers | Product Details
Document History ASTM C1773-21ASTM C1773-17ASTM C1773-13ASTM D3651-02Standard Test Method for Barium in Brackish Water, Seawater, and Brines.. $29.00 $58.00 ASTM D4623-02Standard Test Method for Determination of In Situ Stress in Rock Mass by Overcoring Method-USBM Bore.. $34.00 $67.00 ASTM E1353-02Standard Test Methods for Cigarette Ignition Resistance of Components of Upholstered Furniture.. $33.00 $65.00 |