ASTM E415-08
- standard by ASTM International, 06/01/2008
- Standard Test Method for Atomic Emission Vacuum Spectrometric Analysis of Carbon and Low-Alloy Steel
- Category: ASTM
$60.00
$30.00
Full Description
1.1 This test method covers the simultaneous determination of 20 alloying and residual elements in carbon and low-alloy steels in the concentration ranges shown (Note 1).
Concentration Range, % | ||
Element | Applicable Range, %A | Quantitative Range, %B |
Aluminum | 0 to 0.075 | 0.02 to 0.075 |
Arsenic | 0 to 0.1 | 0.05 to 0.1 |
Boron | 0 to 0.007 | 0.002 to 0.007 |
Calcium | 0 to 0.003 | 0.001 to 0.003 |
Carbon | 0 to 1.1 | 0.08 to 1.1 |
Chromium | 0 to 2.25 | 0.02 to 2.25 |
Cobalt | 0 to 0.18 | 0.008 to 0.18 |
Copper | 0 to 0.5 | 0.04 to 0.5 |
Manganese | 0 to 2.0 | 0.10 to 2.0 |
Molybdenum | 0 to 0.6 | 0.03 to 0.6 |
Nickel | 0 to 5.0 | 0.02 to 5.0 |
Niobium | 0 to 0.085 | 0.02 to 0.085 |
Nitrogen | 0 to 0.015 | 0.004 to 0.015 |
Phosphorous | 0 to 0.085 | 0.02 to 0.085 |
Silicon | 0 to 1.15 | 0.07 to 1.15 |
Sulfur | 0 to 0.055 | 0.01 to 0.055 |
Tin | 0 to 0.045 | 0.01 to 0.045 |
Titanium | 0 to 0.2 | 0.004 to 0.2 |
Vanadium | 0 to 0.3 | 0.004 to 0.3 |
Zirconium | 0 to 0.05 | 0.02 to 0.05 |
A Applicable range in accordance with Guide E 1763 for results reported in accordance with Practice E 1950.
B Quantitative range in accordance with Practice E 1601.
Note 1 - The concentration ranges of the elements listed have been established through cooperative testing of reference materials. Included, in addition to the original data of Test Method E 415 - 71, are data from cooperative testing of a broader range of reference materials to expand the element concentration ranges.
1.2 This test method covers analysis of specimens having a diameter adequate to overlap the bore of the spark stand opening (to effect an argon seal). The specimen thickness can vary significantly according to the design of the spectrometer stand, but a thickness between 10 mm and 38 mm has been found to be most practical.
1.3 This test method covers the routine control analysis in iron and steelmaking operations and the analysis of processed material. It is designed for chill-cast, rolled, and forged specimens. Better perform
Product Details
- Published:
- 06/01/2008
- Number of Pages:
- 9
- File Size:
- 1 file , 110 KB
- Redline File Size:
- 2 files , 210 KB
- Note:
- This product is unavailable in Russia, Ukraine, Belarus
Document History
ASTM E415-21
ASTM E415-17
ASTM E415-15
ASTM E415-14
ASTM E415-08
ASTM E415-99a(2005)
ASTM E415-99a
ASTM E1338-09(2021)
Standard Guide for Identification of Metals and Alloys in Computerized Material Property Databases..
$32.00 $64.00
ASTM D8386-21
Standard Test Method for Determining Enhanced Filter Blocking Tendency (EFBT)..
$26.00 $52.00
ASTM E1982-98(2021)
Standard Practice for Open-Path Fourier Transform Infrared (OP/FT-IR) Monitoring of Gases and Vapor..
$29.00 $58.00
ASTM E1054-21e1
Standard Practices for Evaluation of Inactivators of Antimicrobial Agents..
$34.00 $68.00